Beilstein J. Nanotechnol. 2015, 6, 472–479, doi:10.3762/bjnano.6.48
Figure 1: Schematics of the fabrication of SiO2 coated membranes: (a) irradiation of PC foil with GeV heavy i...
Figure 2: Diffuse reflectance FTIR spectra of uncoated (black) and coated (28 cycles (red), 112 cycles (blue)...
Figure 3: O 1s contributions of polycarbonate to the XP spectra of uncoated (orange, grey dots are measured c...
Figure 4: (a) SEM image of a bundle of highly-flexible SiO2 nanotubes after dissolution of the PC membrane. (...
Figure 5: (a) Small angle X-ray scattering intensities as a function of the scattering vector q for an uncoat...
Figure 6: Contact angle measurements as a function of the number of ALD cycles. With increasing thickness of ...
Beilstein J. Nanotechnol. 2011, 2, 293–301, doi:10.3762/bjnano.2.34
Figure 1: SEM images of aligned CNTs prepared at different temperatures (a) 650 °C, (b) 750 °C, (c) 850 °C, (...
Figure 2: (a) SEM image of aligned CNTs on a quartz substrate. (b) SEM image of an isolated mat collected fro...
Figure 3: X-ray diffraction (XRD) of aligned MWCNTs on quartz substrate prepared at (a) 650 °C and (b) 1100 °...
Figure 4: TEM images of aligned CNTs prepared at (a) 650 °C, (b) 750 °C, (c) 850 °C, (d) 950 °C, (e) 1000 °C,...
Figure 5: HRTEM images of MWCNTs prepared at (a) 650 °C, (b) 750 °C, (c) 850 °C, (d) 950 °C, (e) 1000 °C, and...
Figure 6: AFM image of isolated CNTs prepared at (a) 650 °C and (b) 1100 °C. The scan area is 15 μm × 15 μm a...
Figure 7: SAXS pattern of aligned CNTs prepared at (a) 1100 °C and (b) 650 °C. SEM images of aligned CNTs pre...
Figure 8: (a) Raman spectra and (b) TGA curves of aligned CNTs prepared at 650 and 1100 °C.